hexagonal structure

This is a hexagonal structure in which the two kinds of atom lie in separate layers.

这是一种六角形的结构,两类原子处在分离的层内.

Results show that all the alloys consist of a V-based solid solution main phase with bcc structure and a C14 laves secondary phase with hexagonal structure.

结果表明，当无La替代时，合金主要含有BCC结构的固溶体相以及少量Laves相。

XRD and TEM studies show that the ZnO crystalline in hexagonal structure with spherical particle and uniform size distribution of 8 nm.

结果表明：产物纳米氧化锌为粒度分布均匀的球形六角晶系结构，平均粒径约为8nm。

It is also revealed that the rich Ge films which deposit under higher temperatures exhibit T2 phase with tetragonal structure, while those which deposit under lower temperatures exhibit T phase with hexagonal structure.

发现在较高温度下沉积时，富Ge薄膜往往伴随四方结构T2相存在；相反，在较低温度下沉积时多出现六方结构的σ-Nb5Ge3相。

A flatted dispersion and highly nonlinear photonic crystal fiber with simple hexagonal structure is designed, and the nonlinearity of highly nonlinear photonic crystal fiber is tested.

又设计了简单正六边形结构的平坦双零色散高非线性光子晶体光纤，并且测试了高非线性光子晶体光纤的非线性。

However, the close-packed hexagonal structure of magnesium alloy weakens its plasticity capability and hampers the deformation at ambient temperature that may hinder the further application.

然而，镁合金的密排六方结构使其在室温环境下塑性能力差、变形困难，制约了镁合金的进一步应用。

The results show that these alloys are composed of C14 Laves phase matrix with hexagonal structure and C15 Laves second phase with cubic structure.

结果表明，合金均由六方结构的C14型Laves主相和立方结构的C15型Laves第二相构成；

The result of TEM analysis indicated that the new phase was Mg_3Sb_2 particle, which has the close-packed hexagonal structure.

用透射电镜分析新相的具体组成和结构发现，这种新相是由Mg和Sb生成的金属间化合物Mg3Sb2，具有密排六方结构。

The results showed that the active zinc oxide powder was in cubic and hexagonal structure with spherical shape, its average particle size was 8 nm and its purity was high.

结果表明：活性氧化锌的粒度分布均匀，形貌为近似球形，其平均粒径为80nm，产品纯度高。

The results show that the microstructure of the film is uniform and the grain size is fine. AlN film is the close-packed hexagonal structure with ( 002) preferred orientation.

结果表明膜层组织均匀，晶粒细小，薄膜AIN是呈（002）择优取向的密排六方结构。

For the same dielectric constant ratio, hexagonal structure lattice can obtain a wider complete forbidden band;

对于相同介电常数比，六边形晶格可获得较宽的完全禁带；